WMP-Retro Silver
FOIL / SCRIM / KRAFT / GLASS MAT / FOIL
Tentative Specification
FACING COMPOSITION | DESCRIPTION | VALUES (ENGLISH) | VALUES (Metric) |
---|---|---|---|
Foil | Aluminum | 0.0003 inch | 7.6 micron |
Barrier Coating | Elastomeric Polymer | 0.0001 inch | 2.5 micron |
Reinforcing | Tri-directional Fiberglass | 2 / inch (MD) 3 / inch (XD) | 8 / 100 mm (MD)
12 / 100 mm (XD) |
Adhesive | Flame Resistant | ||
Kraft | Natural | 30 lbs / 3000 ft² | 49 g / m² |
Adhesive | Polymeric | ||
Mat | Fiberglass | 27 lbs / 3000 ft² | 44 g / m² |
Foil | Aluminum | 0.0003 inch | 7.6 micron |
PHYSICAL PROPERTIES | TEST METHOD | VALUES (ENGLISH) | VALUES (Metric) |
---|---|---|---|
Basis Weight | Scale | 40 lbs / 1000 ft² | 195 g / m² |
Permeance (WVTR) | ASTM E96 Procedure A | 0.02 perm (grains/hr. ft². in Hg) | 1.15 ng / N.s |
Bursting Strength | ASTM D774 | 50 psi | 3.5 kg / cm² |
Tensile Strength | ASTM C1136 | 55 lbs/inch width (MD)
25 lbs/inch width (XD) | 9.6 kn / m (MD)
4.4 kn / m (XD) |
Caliper / Thickness | Micrometer | 0.016 inch | 406 micron |
Accelerated Aging | 30 Days @
95% RH,
120°F (49°C) | No Corrosion
No Delamination | No Corrosion
No Delamination |
Low Temperature Resistance | ASTM D1790 -40°F (-40°C) | Remains Flexible
No Delamination | Remains Flexible No Delamination |
High Temperature Resistance | 4 hours @ 240°F (116°C) | Remains Flexible No Delamination | Remains Flexible
No Delamination |
Water Immersion | 24 hours @ 73°F (23°C) | No Delamination | No Delamination |
Mold Resistance | ASTM C665 / C1338 | No Growth | No Growth |
Dimensional Stability | ASTM D1204 | 0.25% | 0.25% |
Light Reflectance | ASTM E408 | 85% | 85% |
FIRE TESTING | ASTM E84 Reinforced Foil Side |
---|---|
Flame Spread | 10 |
Smoke Developed | 15 |
Physical Properties based upon statistical averages, Weight / Thickness +/- 10%