ARENASHIELD
FOIL / FIBERGLASS-POLYESTER
BLEND FABRIC Contents: [Facing Composition] [Physical
Properties] [Fire Testing]
(click for PDF format)
| FACING
COMPOSITION |
DESCRIPTION |
VALUES (ENGLISH) |
VALUES (METRIC) |
| Foil |
Aluminum |
0.0003
inch |
7.6
micron |
| Adhesive |
Flame Resistant |
|
|
| Fabric |
Fiberglass/Polyester Blend |
75 lbs /
3000 ft² |
122 gm /
m² |
| PHYSICAL
PROPERTIES |
TEST METHOD |
VALUES (ENGLISH) |
VALUES (METRIC) |
| Basis Weight |
Scale |
40 lbs / 1000 ft² |
195 gm / m² |
| Permeance (WVTR) |
ASTM E96
Procedure A |
0.02 perm
(grains/hr.ft².in Hg) |
1.15 ng / N.s |
| Bursting Strength |
ASTM D774 |
250 psi |
17.6 kg / cm² |
| Puncture Resistance |
ASTM C1136 |
550 beach units |
16.4 Joules |
| Tensile Strength |
ASTM C1136 |
195 lbs/inch width(MD)
150 lbs/inch width(XD) |
34.1 kn / m (MD)
26.3 kn / m (XD) |
| Caliper / Thickness |
Micrometer |
0.006 inch |
152 micron |
| Accelerated Aging |
30 Days @
95% RH, 120°F (49°C) |
No Corrosion
No Delamination |
No Corrosion
No Delamination |
| Low Temperature Resistance |
ASTM D1790
-40°F (-40°C) |
Remains Flexible
No Delamination |
Remains Flexible
No Delamination |
| High Temperature Resistance |
4 hours @
240°F (116°C) |
Remains Flexible
No Delamination |
Remains Flexible
No Delamination |
| Water Immersion |
24 hours @ 73°F (23°C) |
No Delamination |
No Delamination |
| Mold Resistance |
ASTM C665 /
C1338 |
No Growth |
No Growth |
| Dimensional Stability |
ASTM D1204 |
0.25% |
0.25% |
| Emissivity |
ASTM E408 |
0.03 |
0.03 |
| FIRE TESTING |
UL
723 / ASTM E84 |
CAN
ULC-S102M |
BRITISH
STANDARD 476 |
Flame
Spread |
Smoke
Developed |
Flame
Spread |
Smoke
Developed |
Parts 6 and
7
Summary Report |
| Foil Exposed |
5 |
5 |
5 |
5 |
|
| Fabric Exposed |
5 |
5 |
5 |
5 |
|
Physical Properties based upon statistical
averages, Weight / Thickness +/- 10%
|