3035 BLACK
BLACK COATING / FOIL / SCRIM /
KRAFT
Contents: [Facing Composition] [Physical
Properties] [Fire Testing]
(click for PDF format)
| FACING
COMPOSITION |
DESCRIPTION |
VALUES (ENGLISH) |
VALUES (METRIC) |
| Black Coating |
Flame Resistant |
0.0002 inch |
5.1 micron |
| Foil |
Aluminum |
0.0003 inch |
7.6 micron |
| Barrier Coating |
Elastomeric Polymer |
0.0001 inch |
2.5 micron |
| Reinforcing |
Tri-directional
Fiberglass |
2 / inch (MD) 3 / inch (XD) |
8 / 100 mm (MD) 12 /
100 mm (XD) |
| Adhesive |
Emulsion |
|
|
| Kraft |
Natural |
30 lbs. / 3000 ft² |
48 g / m² |
| PHYSICAL
PROPERTIES |
TEST METHOD |
VALUES (ENGLISH) |
VALUES (METRIC) |
| Basis Weight |
Scale |
21 lbs / 1000 ft² |
103 gm / m² |
| Permeance (WVTR) |
ASTM E96
Procedure A |
0.02 perm
(grains/hr.ft².in Hg) |
1.15 ng / N.s |
| Bursting Strength |
ASTM D774 |
40 psi |
2.8 kg / cm² |
| Puncture Resistance |
ASTM C1136 |
25 beach units |
0.7 Joules |
| Tensile Strength |
ASTM C1136 |
- 40
lbs/inch width (MD)
-
25 lbs/inch width (XD)
|
-
7.0 kN /
m (MD)
-
4.4 kN / m (XD)
|
| Caliper / Thickness |
Micrometer |
0.007 inch |
178 micron |
| Accelerated Aging |
30 Days @
95% RH, 120°F (49°C) |
No Corrosion
No Delamination |
No Corrosion
No Delamination |
| Low Temperature Resistance |
ASTM D1790
-40°F (-40°C) |
Remains Flexible
No Delamination |
Remains Flexible
No Delamination |
| High Temperature Resistance |
4 hours @
240°F (116°C) |
Remains Flexible
No Delamination |
Remains Flexible
No Delamination |
| Water Immersion |
24 hours @ 73°F (23°C) |
No Delamination |
No Delamination |
| Mold Resistance |
ASTM C665 / C1338 |
No Growth |
No Growth |
| Dimensional Stability |
ASTM D1204 |
0.25% |
0.25% |
| FIRE TESTING |
UL
723 / ASTM E84 |
CAN
ULC-S102M |
BRITISH
STANDARD 476 |
Flame
Spread |
Smoke
Developed |
Flame
Spread |
Smoke
Developed |
Parts 6 and
7
Summary Report |
| Black Coating
Exposed |
0 |
0 |
|
|
|
Physical Properties based upon statistical
averages, Weight / Thickness +/- 10%
|